DuPont Performance Polymers Zytel® HTN 52G35HSL NC010Polyphthalamide (PPA)
Polymer,Thermoplastic,Polyphthalamide (PPA),Polyphthalamide (PPA), 40% Glass Fiber ReinforcedDuPont Performance Polymers
产品说明
Zytel® HTN52G35HSL NC010 is a 35% glass reinforced, heat stabilized, lubricated high performance polyamide resin that can be molded in water heated molds.Information provided by DuPontPerformance Polymers
物理性能
比重密度填料含量线性成型收缩率
额定值 (公制)
1.47 g/cc1.45 g/cc35 %
0.0025 cm/cm
@Thickness 1.60 mm0.0030 cm/cm
@Thickness 3.20 mm0.010 cm/cm
@Thickness 1.60 mm0.010 cm/cm
@Thickness 3.20 mm
额定值 (英制)
1.47 g/cc0.0524 lb/in³35 %
0.0025 in/in
@Thickness 0.0630 in0.0030 in/in
@Thickness 0.126 in0.010 in/in
@Thickness 0.0630 in0.010 in/in
@Thickness 0.126 in0.0020 in/in
@Thickness 0.0787 in
测试方法
DAM; ASTM D792DAM; ISO 1183DAMFlow; DAM
Flow; DAM
Transverse; DAM
Transverse; DAM
线性成型收缩率,Flow
0.0020 cm/cm
@Thickness 2.00 mm
DAM; ISO 294-4
机械性能
洛氏硬度(M 级)洛氏硬度(R 级)抗张强度(断裂)
额定值 (公制)
105124
180 MPa
@Temperature 23.0 °C200 MPa
@Temperature 23.0 °C
额定值 (英制)
105124
26100 psi
@Temperature 73.4 °F29000 psi
@Temperature 73.4 °F10500 psi
@Temperature 392 °F11600 psi
@Temperature 347 °F12900 psi
@Temperature 302 °F18000 psi
@Temperature 212 °F24400 psi
@Temperature 73.4 °F27300 psi
@Temperature 140 °F29600 psi
@Temperature 73.4 °F33400 psi
@Temperature -40.0 °F
3128 psi
@Strain 0.210 %, Temperature 73.4 °F3403 psi
@Strain 0.510 %, Temperature 302 °F3526 psi
@Strain 0.210 %, Temperature 32.0 °F3562 psi
@Strain 0.220 %, Temperature 104 °F3572 psi
@Strain 0.200 %, Temperature -4.00 °F3749 psi
@Strain 0.210 %, Temperature -4.00 °F3774 psi
@Strain 0.510 %, Temperature 248 °F37 psi
@Strain 0.230 %, Temperature 32.0 °F3920 psi
@Strain 0.520 %, Temperature 302 °F
测试方法
DAM; ASTM D785DAM; ASTM D78550%RH; ISO 527
DAM; ISO 527
抗张强度
72.4 MPa
@Temperature 200 °C80.0 MPa
@Temperature 175 °C.0 MPa
@Temperature 150 °C124 MPa
@Temperature 100 °C168 MPa
@Temperature 23.0 °C188 MPa
@Temperature 60.0 °C204 MPa
@Temperature 23.0 °C230 MPa
@Temperature -40.0 °C
21.57 MPa
@Strain 0.210 %, Temperature 23.0 °C23.46 MPa
@Strain 0.510 %, Temperature 150 °C24.31 MPa
@Strain 0.210 %, Temperature 0.000 °C24.56 MPa
@Strain 0.220 %, Temperature 40.0 °C24.63 MPa
@Strain 0.200 %, Temperature -20.0 °C25.85 MPa
@Strain 0.210 %, Temperature -20.0 °C26.02 MPa
@Strain 0.510 %, Temperature 120 °C26.87 MPa
@Strain 0.230 %, Temperature 0.000 °C27.0 MPa
@Strain 0.520 %, Temperature 150 °C
DAM; ASTM D638
DAM; ASTM D638
DAM; ASTM D638
DAM; ASTM D638
50%RH; ASTM D638
DAM; ASTM D638
DAM; ASTM D638
DAM; ASTM D638
DAM; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2
本页面信息资料来自厂商，文档提供者不承担任何法律责任，强烈建议在最终选择材料前，就数据值与材料供应商进行验证。版权归原作者所有，如有侵权请立即与我们联系。Page 1
29.31 MPa
@Strain 0.270 %, Temperature 60.0 °C29.53 MPa
@Strain 0.260 %, Temperature 23.0 °C30.36 MPa
@Strain 0.520 %, Temperature 90.0 °C31.33 MPa
@Strain 0.480 %, Temperature 120 °C33.66 MPa
@Strain 0.430 %, Temperature 90.0 °C33.8 MPa
@Strain 0.480 %, Temperature 60.0 °C33.82 MPa
@Strain 0.370 %, Temperature 40.0 °C40.0 MPa
@Strain 1.01 %, Temperature 150 °C44.91 MPa
@Strain 1.02 %, Temperature 120 °C45.14 MPa
@Strain 0.400 %, Temperature 23.0 °C46.55 MPa
@Strain 1.03 %, Temperature 150 °C47.58 MPa
@Strain 0.400 %, Temperature 0.000 °C48.33 MPa
@Strain 0.420 %, Temperature 40.0 °C48.71 MPa
@Strain 0.400 %, Temperature -20.0 °C51.27 MPa
@Strain 1.52 %, Temperature 150 °C52.09 MPa
@Strain 1.02 %, Temperature 90.0 °C52.74 MPa
@Strain 0.430 %, Temperature -20.0 °C52.86 MPa
@Strain 0.440 %, Temperature 0.000 °C56.27 MPa
@Strain 0.970 %, Temperature 120 °C57.13 MPa
@Strain 0.520 %, Temperature 60.0 °C57.71 MPa
@Strain 1.50 %, Temperature 120 °C58.76 MPa
@Strain 0.510 %, Temperature 23.0 °C59.16 MPa
@Strain 2.00 %, Temperature 150 °C59.45 MPa
@Strain 0.940 %, Temperature 60.0 °C60.05 MPa
@Strain 1.54 %, Temperature 150 °C60.37 MPa
@Strain 0.840 %, Temperature 90.0 °C63.4 MPa
@Strain 0.730 %, Temperature 40.0 °C65.23 MPa
@Strain 2.50 %, Temperature 150 °C67.45 MPa
@Strain 2.01 %, Temperature 120 °C67.85 MPa
@Strain 1.54 %, Temperature 90.0 °C69.31 MPa
@Strain 0.600 %, Temperature 23.0 °C69.59 MPa
@Strain 3.01 %, Temperature 150 °C69.78 MPa
@Strain 2.05 %, Temperature 150 °C71.76 MPa
@Strain 0.600 %, Temperature 0.000 °C
4251 psi
@Strain 0.270 %, Temperature 140 °F4283 psi
@Strain 0.260 %, Temperature 73.4 °F4403 psi
@Strain 0.520 %, Temperature 194 °F4544 psi
@Strain 0.480 %, Temperature 248 °F4882 psi
@Strain 0.430 %, Temperature 194 °F4900 psi
@Strain 0.480 %, Temperature 140 °F4905 psi
@Strain 0.370 %, Temperature 104 °F5800 psi
@Strain 1.01 %, Temperature 302 °F6514 psi
@Strain 1.02 %, Temperature 248 °F6547 psi
@Strain 0.400 %, Temperature 73.4 °F6752 psi
@Strain 1.03 %, Temperature 302 °F6901 psi
@Strain 0.400 %, Temperature 32.0 °F7010 psi
@Strain 0.420 %, Temperature 104 °F7065 psi
@Strain 0.400 %, Temperature -4.00 °F7436 psi
@Strain 1.52 %, Temperature 302 °F7555 psi
@Strain 1.02 %, Temperature 194 °F79 psi
@Strain 0.430 %, Temperature -4.00 °F7667 psi
@Strain 0.440 %, Temperature 32.0 °F8161 psi
@Strain 0.970 %, Temperature 248 °F8286 psi
@Strain 0.520 %, Temperature 140 °F8370 psi
@Strain 1.50 %, Temperature 248 °F8522 psi
@Strain 0.510 %, Temperature 73.4 °F8580 psi
@Strain 2.00 %, Temperature 302 °F8623 psi
@Strain 0.940 %, Temperature 140 °F8710 psi
@Strain 1.54 %, Temperature 302 °F8756 psi
@Strain 0.840 %, Temperature 194 °F9200 psi
@Strain 0.730 %, Temperature 104 °F9461 psi
@Strain 2.50 %, Temperature 302 °F9783 psi
@Strain 2.01 %, Temperature 248 °F9841 psi
@Strain 1.54 %, Temperature 194 °F10050 psi
@Strain 0.600 %, Temperature 73.4 °F10090 psi
@Strain 3.01 %, Temperature 302 °F10120 psi
@Strain 2.05 %, Temperature 302 °F10410 psi
@Strain 0.600 %, Temperature 32.0 °F
DAM; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2
DAM; ISO 11403-1/-2
本页面信息资料来自厂商，文档提供者不承担任何法律责任，强烈建议在最终选择材料前，就数据值与材料供应商进行验证。版权归原作者所有，如有侵权请立即与我们联系。Page 2
72.71 MPa
@Strain 3.51 %, Temperature 150 °C72.74 MPa
@Strain 0.0 %, Temperature 40.0 °C
10550 psi
@Strain 3.51 %, Temperature 302 °F10550 psi
@Strain 0.0 %, Temperature 104 °F
50%RH; ISO 11403-1/-2
DAM; ISO 11403-1/-2